利用不同的方法分别合成了常规尺寸和纳米NaY分子筛,并采用XRD和TEM手段对合成样品进行了表征,小晶粒分子筛其粒径小于100 nm。催化裂化试验表明,纳米分子筛可提高大分子转化能力及改善产物选择性,比常规晶粒尺寸分子筛更为优越的性能。
Abstract：NaY zeolites with nanosize and normal size were successfully synthesized through different ways.The X-ray diffraction and TEM results indicated that the crystal zeolite product had an average size under 100 nm.Fluid catalytic cracking(FCC) catalysts was prepared respectively from the two zeolites.FCC test results showed that compared with catalyst containing conventionally hydrothermal synthesized NaY zeolite,catalyst containing nanosized zeolite exhibited good big molecule cracking performance and excellent selectivity.
[1]RAJAGOPALAN K,PETERS A W,EDWARDS G C.Influence of zeolite particle-size on selectivity during fluidcatalytic cracking[J].Appl Catal,1986,23(1):69-99.
[2]SHIRALKAR V P,JOSHI P N,EAPEN M J,et al.Synthesisof ZSM-5 with variable crystallite size and its influence onphysicochemical properties[J].Zeolites,1991,11:511-516.
[3]PU S B,INUL T.Influence of crystallite size on catalyticperformance of HZSM-5 prepared by different methods in 2,7-dimethylnaphthalene isomerization[J].Zeolites,1996,17:334-339.
[4]HERRMANN C,HAAS J,FETTING F.Effect of the crystalsize on the activity of ZSM-5 catalysts in various reactions[J].Appl Catal,1987,35:299-310.
[5]VALTCHEV V,MINTOVA S,DIMOV V,et al.Tribochemical activation of seeds for rapid crystallization ofzeolite Y[J].Zeolites,1995,15:193-197.
[6]DUTTA P K,BRONIC J.Mechanism of zeolite formation-seed gel interaction[J].Zeolites,1994,14:250-255.
[7]SCHOEMAN B J,STERTE J,OTTERSTEDT J E.Synthesisand size tailoring of colloidal zeolite particles[J].J ChemSoc,Chem Commun,1993,12:994-995.
[8]MCDANIED C V,MAHER P K,PILATO J M.Preparation ofzeolites[P].US:4 166 099,1979-08-28.
[9]LINDNER T,LECHERT H.Chelate ligands as mineralizingagents in hydrothermal synthesis of faujasite-type zeolites:Akinetic study[J].Zeolites,1996,16:196-206.
[10]SCHOEMAN B J,STERTE J,OTTERSTEDT J E.Colloidalzeolite suspensions[J].Zeolites,1994,14:110-116.
[11]LECHERT H,KACIREK H.Investigations on thecrystallization of X-type zeolites[J].Zeolites,1991,11:720-728.
基本信息:
中图分类号:O643.32
引用信息:
[1]吴杰,秦永宁,马智,等.由煤系高岭土合成小晶粒NaY分子筛及其应用[J].化学工业与工程,2006(01):18-20.
基金信息:
中国石油化工总公司资助项目(项目编号:X503007)
2006-01-30
2006-01-30